The transport of Cr(VI) from chrome plating water by polymer inclusion membrane based carbon nanomaterial

In this study, we have implemented; Cr (VI), which is used in the chromate plating process in the plating industry and is highly toxic to the environment, has been removed from the chromate plating water by using an enhanced polymer inclusion membrane with modifiyinggraphane oxide (GO/PIM) which is increased mechanical structure and permeability of PIM.The synthesized graphene oxide was characterized by TEM, SEM, IR, Raman, XRD and XPS.In the study, the optimum amount of graphene oxide in the modified membrane was determined and the membrane lifetime and the mechanical stability of the membrane were investigated in GO / PIM experiments. It was obtained highly selective and a high recovery value of 96.83 % for the removal of Cr(VI) ions from the chromate plating water with synthesized GO/ PIM.This research contributes the production of new generates membranes in our country in the near feature with increasing of the mechanical stability and the membrane lifetime of the GO/PIM and on the usability of these membranes in industrial applications.

Kromat kaplama suyundan Cr(VI)'nýn karbon bazlý nanomalzeme içeren polimer içerikli membran ile transportu

Gerçekleþtirilen çalýþma ile kaplama sanayinde kromatlama prosesinde kullanýlan ve çevre için oldukça toksik bir özelliðe sahip olan Cr(VI)’nýn, kromat kaplama suyundan mekanik özellikleri ve geçirgenliði grafen oksitle modifiye edilerek arttýrýlmýþ polimer içerikli membran (GO/PIM) kullanýlarak uzaklaþtýrýlmasý saðlanmýþtýr. Sentezlenen grafen oksit TEM, SEM, IR, Raman, XRD ve XPS ile karakterize edilmiþtir. Çalýþmada, modifiye edilen membrandaki optimum grafen oksit miktarý belirlenmiþ ve GO/PIM ile gerçekleþtirilen deneylerde membran kullaným ömrü ve membranýn mekaniksel kararlýlýðý araþtýrýlmýþtýr. Sentezlenen GO/PIM kromat kaplama sularýndan Cr(VI) iyonlarýnýn uzaklaþtýrýlmasý ve arýtýmý için oldukça seçici ve %96.83 gibi yüksek bir geri kazaným deðeri elde edilmiþtir. GO/PIM'in mekanik kararlýlýðýnýn ve membran ömrünün artmasý ile yeni nesil membranlarýn yakýn gelecekte ülkemizde üretilebilir hale gelmesine ve bu membranlarýn endüstriyel uygulamalarda kullanýlabilirliðine yönelik bir araþtýrma gerçekleþtirilmiþtir.