Application of polyoxometalate/carbon nitride nanotubes nanocomposite for directly methanol oxidation

Fuel cell in this study consumes methanol as fuel and they are very important for clean environment and effective energy conversion. Graphitic carbon nitride (g-C3N4) is carbon allotrope among carbon based nanomaterials. It consists of C−N bonds in π-based polymer. Polyoxometalates (POMs) are redox-active materials and have crucial potential for direct methanol oxidation and energy storage. POMs attract important interest because they included in high-valent metals and anionic metal oxides. In present report, the nanocomposite of polyoxometalate/C3N4 NTs was synthesized and applied for fuel cell. Firstly, the structure of prepared nanocomposite was investigated by transmission electron microscope (TEM), x-ray photo electron spectroscopy (XPS) and scanning electron microscope (SEM). After that, the voltammetric measurements were performed by using nanocomposite modified electrode. The electrochemical active areas of POM-C3N4 NTs/GCE and C3N4 NTs/GCE are 0.511 cm2 and 0.169 cm2, respectively. The prepared nanocomposite demonstrated active catalytic effect towards methanol.

Doðrudan metil alkol oksidasyonu için polioksometalat/karbon nitrit nanotüp nanokompozitinin uygulanmasý

Grafit karbon nitrit (g-C3N4) karbon bazlý nanomateryaller arasýnda kararlý karbon allotropudur. Π bazlý polimer sisteminde elektron lokalizasyonu olmayan C − N baðlarýndan oluþur. Polioksometalatlar (POMs) redoks-aktif maddelerdir ve doðrudan metanol oksidasyonu ve enerji depolama için hayati bir potansiyele sahiptir. POM'lar, yüksek deðerli metaller ve anyonik metal oksitler içerdikleri için ilgi görmektedir.Bu çalýþmada, Polioksometalat/ karbon nitrit nanotüp (C3N4 NTs) sentezlenmiþ ve yakýt hücresi için uygulanmýþtýr. Öncelikle, hazýrlanan nanokompozitin yapýsý geçirgen elektron mikroskopu (TEM), x-ýþýnlarý fotoelektron spektroskopisi (XPS) ve taramalý elektron mikroskopu (SEM) kullanýlarak incelenmiþtir. Daha sonra bu nanokompozit modifiyeli elektrot kullanýlarak elektrokimyasal ölçümler gerçekleþtirilmiþtir. POM-C3N4 NTs/GCE ve C3N4 NTs/GCE elektrotlarýn elektrokimyasal aktif yüzeyleri sýrasýyla 0.511 cm2 ve 0.169 cm2 olarak bulunmuþtur. Hazýrlanan nankompozit metil alkole karþý aktif bir katalitik etki göstermiþtir.