EFFECTS OF INCLUSIONS ON AN Al-Cu 4-Mg1.5 ALLOY

Filtering through refractory material is accepted as an efficient method for the removal of inclusions from the structure of aluminum-base alloys. The effects of inclusions are examined in relation to the anisotropy of the wrought aluminum alloy, Al – Cu 4 – Mg 1.5. The experimental variables selected were the filtration technique, casting methods, variations in heat treatments as well as variations in rolling reductions. Reduction in the solid particle inclusion content could be achieved by using sintered filter material. Quite high short transverse ductility could be achieved in rolled plates of commercial high strength aluminum alloy.

ÝNKLÜZYONLARIN Al-Cu 4-Mg 1.5 ALAÞIMI ÜZERÝNDEKÝ ETKÝLERÝ

Alüminyum esaslý alaþýmlarýn yapýlarýndan inklüzyonlarýn giderilmesi için refrakter bir malzeme içerisinden filtrasyon tekniði etkin bir yöntem olarak kabul edilmektedir. Ýnklüzyonlarýn etkileri þekillendirilmiþ Al-Cu4-Mg1.5 alaþýmýndaki anizotropi ile iliþkili olarak incelenmiþtir. Seçilen deney deðiþkenleri filtrasyon teknikleri, farklý döküm yöntemleri, farklý ýsýl iþlemler ve þekil deðiþim oranýndaki farklýlýklar olmuþtur. Sinterlenmiþ filtre malzemesi kullanarak katý partikül inklüzyonlarýnda azalma saðlanmýþtýr. Ticari kalitede yüksek mukavemetli alüminyum alaþýmlarýnda haddelenmiþ yapýda kesitten alýnan numunelerde yüksek süneklik deðerleri elde edilmiþtir.