EFFECT OF MECHANICAL PROPERTIES OF MARTENSITE AND LOADING RATE ON DUAL PHASE STEELS

In this study, steel sheet materials were used in order to obtain dual-phase steel. Specimens for this purpose have been annealed in ferrite + astatine regions at the temperatures of 740, 760, 800 and 820 °C. The specimens were annealed at the different temperatures with corresponding times 20, 40 and 60 minutes and quenched into water. As a result of this dual-phase steels at different ferrite + martensite ratio were produced. Sheet specimens were tested at the range of loading rates of 10, 50 and 259 mm/min. Strength properties of dual-phase steels were investigated depending on annealing temperature, ratio of martensite and loading rate.

DUAL FAZLI ÇELÝKLERDE MARTENZÝT VE YÜKLEME HIZININ MEKANÝK ÖZELLÝKLERE ETKÝSÝ

Bu çalýþmada, dual fazlý çelik elde etmek için çelik saç malzemeler kullanýlmýþtýr. deneysel çalýþmalarýn gerektirdiði ölçülerde hazýrlanan numuneler ferrit + ostenit bölgesinde farklý sýcaklýklarda (740, 760, 800, 820 °C) tavlanmýþlardýr. Herbir sýcaklýkta numuneler 20, 40 ve 60 dakika tavlama sürelerinde tavlanarak suda su verilmiþtir. Seçilen tavlama programýna baðlý olarak martenzit ve ferrit oranlarý farklý dual fazlý çelikler elde edilmiþtir. Saç numuneler 10, 50 ve 250 mm/dak’ lýk yükleme hýzlarýnda testlere tabi tutularak çekme dayanýmlarý belirlenmiþtir. Söz konusu dual fazlý çeliklerin çekme özellikleri tavlama sýcaklýðýna, martenzit oranýna ve yükleme hýzýna baðlý olarak incelenmiþtir.