DEFORMATION TEXTURES IN A COPPER NICKEL ALLOY

Non-random distribution of orientations between the neigbouring grains of polycrystalline aggregates leads to preferred orientations or textures. Texture analysis of a Cu-10 % Ni alloy carried out on three types of cast materials after varying amounts of deformation led to clearly defined copper type texture due to the dominance of high stacking fault energy SFE regions in the structure. (123) [41 2 ] is the strongest orientation observed with (123) as the plane lying paralel to the rolling plane and [41 2 ] as the direction paralel to the rolling direction.

BAKIR NÝKEL ALAÞIMLARINDA DEFORMASYON ÖRGÜSÜ

Polikristalin malzemelerde komþu taneler arasýndaki yerleþim iliþkileri tercihli yerleþim veya örgüyü ortaya çýkarýr. Üç farklý tip döküm prosesi ve farklý deformasyon seviyeleri sonrasý Cu-% 10 Ni alaþýmlarýndan alýnan numuneler üzerinde yapýlan analiz, yapýda hakim durumda olan yüksek istif hatasý enerjisinden dolayý bakýr tipi örgüyü açýk bir þekilde ortaya çýkarmýþtýr. Gözlenen en kuvvetli yerleþim, haddeleme düzlemine paralel (123) düzlemi ve haddeleme yönüne paralel [41 2 ] yönünden oluþan (123) [41 2 ] olmuþtur.