EFFECTS OF SOME BORON COMPOUNDS AND/OR WATER REPELLENTS ON THE HIGROSCOPICITY OF BRUTIA PINE (Pinus brutia Ten.) WOOD

As a water borne salt type, boron salts also tend to increase in hygroscopicity of wood. This phonomenon is known as one of the disadvantages of these salts in wood preservation in spite of their protective effectiveness against biological agents and fire. This study was designed to determine the rate of higroscopicity both treated and untreated Brutia pine wood. Impregnation solutions of boric acid (BA) and sodium perborate (SP) was prepared by water and polyethylene glycol (PEG)-400 (P4). Additionally, some water repellents (WRs) such as paraffin wax (P), styrene (St), methylmethacrylate (MMA) and isocyanate (ISO) were used to keep the hygroscopicity level of wood at an acceptable level. Results indicated that paraffin wax and WRs were considerably lowered the hygroscopicity of wood. 4 homogenity groups were formed from the statistical analysis as follows (from the most hygroscopic treatments to lesser, respectively): (1) P4, (2) P4+BA or SP, control, (3) WRs, BA or SP+WRs and, (4) P+BA+Bx (% 15 aqueous solution). None of the solutions increased the hygroscopicity of wood than control treatments, but P4 (P? 0.05).

BAZI BORLU BÝLEÞÝKLERÝN VE SU ÝTÝCÝ MADDELERÝN KIZILÇAM ODUNUNUN HÝGROSKOPÝSÝTESÝ ÜZERÝNE ETKÝLERÝ

Bu çalýþma; fungisit, insektisit ve yangýn önleyici olumlu etkileri bilinen borlu maddelerden borik asit (BA) ve sodyum perborat (SP)'ýn, odunda higroskopisiteyi ne ölçüde etkilediðinin belirlenmesi amacýyla gerçekleþtirilmiþtir. Suda çözünen tuz formülasyonlarý içerisinde yer alan borlu maddelerin, higroskopisitede neden olduklarý muhtemel artýþýn engellenebilmesi amacýyla; BA ve SP'ýn sulu çözeltileri yanýnda, PEG-400 (P4)'de çözündürülerek hazýrlanmýþ preparatlarý, parafin (P)'le birlikte hazýrlanan % 15'lik sulu çözeltisi ve su itici maddeler (SÝM)'den, stiren (St), metilmetakrilat (MMA) ile izosiyanat (ISO)'la birlikte tek ve ikili iþlemli emprenyelerde kullanýlan birçok çözeltileri hazýrlanmýþtýr. Araþtýrma sonuçlarý, BA ve SP'ýn tam kuru oduna oranla % 0.69-4.60 gibi düþük retensiyonlarýna karþýlýk, bunlardan anlamlý derecede (P?0.05) farklý olmak üzere P4'lü çözeltiler ve SÝM'de % 20-60 gibi yüksek retensiyon oranlarý elde edildiðini göstermiþtir. Retensiyon oranlarý üzerindeki belirleyici etkenin çözücü madde olduðu ortaya çýkarken, higroskopisite açýsýndan 4 farklý homojenlik grubu oluþmuþtur. Bunlar, higroskopisiteyi en çok artýran maddelerden baþlayarak; (1) P4, (2) P4+BA veya SP, Kontrol, (3) SÝM, BA veya SP+SÝM ve (4) P+BA+Bx'týr. Böylece, P4 dýþýnda hiçbir uygulamanýn odunda kontrole oranla higroskopisiteyi önemli derecede ( P? 0.05) artýrmadýðý belirlenmiþtir.