Manufacturing and characterization of aluminium-magnesium macrocomposite by co-extrusion

In this study, aluminum-magnesium macrocomposite containing millimetre scale pure magnesium chips reinforcement was fabricated. The composite was extruded at 400 °C with an extrusion ratio of 9: 1. Characterization of the macrocomposites was carried out by microscopic examinations, density and hardness measurements. This work demonstrated that not only the structural integrity between aluminum alloy and magnesium chips but also the possibility of the solid state recycling of magnesium chips can be provided.

Eþ kalýp ekstrüzyon yöntemi ile alüminyum-magnezyum makrokompozit imalatý ve karakterizasyonu

Bu çalýþmada, eþ kalýp ekstrüzyon yöntemi ile boyutu milimetre aralýðýnda deðiþen ticari kalitede saf magnezyum talaþýný takviye elemaný olarak kullanarak alüminyum/magnezyum makrokompozit üretilmiþtir. Kompozit karýþýmý 400 °C’de 9: 1 ekstrüzyon oranýnda ektrüzyon iþlemine tabi tutulmuþtur. Makrokompozitin karakterizasyonu mikroyapýsal inceleme, yoðunluk ve sertlik ölçümleri ile gerçekleþtirilmiþtir. Karakterizasyon sonucunda alüminyum alaþýmý ve magnezyum talaþý arasýnda yapýsal bütünlüðün saðlandýðý ve magnezyum talaþýnýn katý halde geri kazanýlabileceði tespit edilmiþtir.