Investigation of mechanical properties AISI 1040 steel welding with electric arc and MIG, applied various heat treatments

In this study, AISI 1040 welding samples were produced by arc welding and MIG. The full annealing, normalizing, tempering and stress relief annealing treatment was applied for as-received and welded samples. Made process and untreated samples tensile, three point bending, impact and hardness tests were conducted. Tensile strain of the welded parts is higher than in the welded parts. The yield and tensile strength of the as-received and electric arc welded sample has similar value after stress relief treatment. Hard martensitic structure on the outside, inside is seen increasingly become a soft structure. Increasing in hardness was observed starting from the weld filler metal to outside.

Elektrik ark ve gazaltý kaynaðý (MIG) ile birleþtirilmiþ AISI 1040 çeliðinin mekanik özelliklerine, çeþitli ýsýl iþlemlerin etkisinin incelenmesi

Bu çalýþmada; AISI 1040 çeliði, elektrik ark ve MIG ile kaynatýlýp, numuneler üretilmiþtir. Kaynaklý ve kaynaksýz numuneler tam tavlama, normalizasyon, meneviþleme ve gerilim giderme iþlemlerine tabi tutulmuþlardýr. Ýþleme tabi tutulan ve herhangi bir ýsýl iþlem yapýlmayan numunelere çekme, üç nokta eðme, çentik darbe ve sertlik testleri yapýlmýþtýr. Numunelerin çekme þekil deðiþtirmeleri kaynaksýz parçalarýn, kaynaklý parçalara nazaran daha yüksek elde edilmiþtir. Kaynaksýz ve elektrik ark kaynaðý yapýlýp, gerilim giderme iþlemi görmüþ numunelerin akma ve çekme dayaným deðerleri birbirlerine yakýn elde edilmiþtir. Martenzitik yapýnýn dýþarýda sert, içeri gittikçe yumuþak bir yapý haline geldiði görülmüþtür. Ölçülen sertlik deðerlerinin, kaynak dolgu metalinin ortasýndan baþlayýp genelde dýþarýya doðru bir artýþ gösterdiði gözlenmiþtir.