Effect of different curing conditions on flexural and compressive strength of fly ash mortars

In this study the effect of accelerated curing on the early flexural and compressive strengths of fly ash mortars were investigated. In the mortar mixtures CEM I 42.5 R type cement and C class C fly ash with different proportions were used. 40/40/160 mm prismatic specimens were prepared from these mortars. The mortar samples cured at 7 different curing conditions. Curing conditions are standard curing, 35 °C and 85 °C hot water curing. These curing conditions applied on specimens for different times. Flexural and compressive strengths were performed on the mortar specimens. Obtained test results were comparatively evaluated. The results of this study revealed that, early age strength gain under standard curing conditions due to fly ash inclusion can be compensated by accelerated curing.

Farklý kür yöntemlerinin uçucu kül içeren harçlarýn eðilme ve basýnç dayanýmýna etkisi

Bu çalýþmada; farklý miktarlarda uçucu kül içeren harçlarýn erken yaþlardaki basýnç ve eðilme dayanýmlarýna hýzlandýrýlmýþ kür uygulamalarýnýn etkisi incelenmiþtir. Harç karýþýmlarýnda; baðlayýcý olarak CEM I 42.5 R tip çimento ve deðiþik oranlarda C sýnýfý uçucu kül kullanýlmýþtýr. Üretilen harçlardan 40/40/160 mm ayrýtlý prizmatik örnekler dökülerek 7 farklý kür uygulamasýna tabi tutulmuþtur. Kür uygulamalarý standart kür, 35 °C ve 85 °C’de sýcak su kürü þeklinde ve farklý sürelerde yapýlmýþtýr. Uygulanan kür iþlemleri sonrasýnda harç örnekler üzerinde ortadan tekil yüklemeli eðilme ve eðilme sonrasý tek eksenli basýnç deneyleri gerçekleþtirilmiþtir. Elde edilen sonuçlar karþýlaþtýrmalý olarak deðerlendirilmiþtir. Çalýþma sonucunda; standart kür koþullarý altýnda uçucu kül ikamesinin erken yaþta oluþturduðu basýnç dayaným kaybýnýn sýcak su kürü uygulamasý ile telafi edilebileceði görülmüþtür.