Investigation of the Effects of Hot Dip Aluminizing on Microstructural and Tribological Properties of Dual Phase (DP800) Steels

Yakup Yürektürk, Cansu Çeltik
Bursa Technical University

In this study, the effects of hot-dip aluminizing (HDA) (90 sec at 725°C) and post-heat treatment on the microstructural and tribological properties of DP800 steel were investigated. After HDA treatment, one of the sample was left to cool in air (HDA-1) and the other one left to cool in air after being subjected to a heat treatment for 1 hour in an oven set at 300°C (HDA-2). Evolution in mechanical properties depending on the developments in the coating microstructure investigated in terms of hardness and wear behaviour. Characterization results show that heat treatment increases the hardness value of hot dip aluminized steel to 1100 HV values. Considering the wear ball volume and friction coefficients, the most advanced tribological properties were observed in the heat-treated HDA process (HDA-2).

Keywords: DP800 steel, Hot-dip aluminizing, Heat treatment, Wear

---

Sýcak Daldýrma Alüminyumlama iþleminin Çift Fazlý (DP800) Çeliklerin Mikroyapýsal ve Tribolojik Özelliklerine Etkilerinin Ýncelenmesi

Yakup Yürektürk, Cansu Çeltik
Bursa Teknik Üniversitesi

Bu çalýþmada, sýcak daldýrmalý alüminyumlama (HDA) (725°C'de 90 saniye) ve ardýl ýsýl iþlemin DP800 çeliðinin mikroyapýsal ve tribolojik özellikleri üzerindeki etkileri incelenmiþtir. HDA iþleminden sonra numunelerden biri havada (HDA-1), diðeri ise 300°C'ye ayarlanmýþ etüvde (HDA-2) 1 saat ýsýl iþleme tabi tutularak havada soðumaya býrakýlmýþtýr). Kaplama mikroyapýsýndaki geliþmelere baðlý olarak geliþen mekanik özellikler sertlik ve aþýnma davranýþý bakýmýndan incelenmiþtir. Karakterizasyon sonuçlarý, ýsýl iþlemin sýcak daldýrma alüminize çeliðin sertlik deðerini 1100 HV deðerlerine çýkardýðýný göstermektedir. Aþýnan bilye hacmi ve sürtünme katsayýlarý dikkate alýndýðýnda en geliþmiþ tribolojik özellikler ýsýl iþlem görmüþ HDA prosesinde (HDA-2) gözlenmiþtir.

Anahtar Kelimeler: DP800 çelik, Sýcak daldýrma alüminyumlama, Isýl iþlem, Aþýnma

---