The Microstructure and Hardness Properties Analysis of Welded Aluminum Matrix Material Reinforced with SiC Using Different Currents and Forms of Welding

The welding of metal matrix material reinforced with ceramic particles has some problems such as formation of oxide layer, segregation occurring on welding area, and reaction of ceramic particles with welding bath. The expected mechanical properties cannot be obtained because of these problems. In this study, the weldability of aluminum 2014 alloy reinforced with SiC particles was investigated. MIG welding process was used via using AlSi5 alloy wire at different types and values of welding currents. Samples obtained using manual welding current were compared to those obtained using pulse welding current, in terms of microstructure and distribution of hardness. The effects of different types and values of welding currents on the microstructure and hardness distribution were examined. It was obtained that the welding of the composite with aluminum 2014 alloy matrix reinforced with SiC particles via using of pulse current, potential formation of segregation was prevented and microstructural properties were improved.

SiC Takviyeli Alüminyum Matrisli Kompozit Malzemenin Farklý Kaynak Akýmlarý ve Türlerinde Oluþan Mikroyapý ve Sertlik Özelliklerinin Analizi

Metal matrisli ve seramik partikül takviyeli malzemelerin kaynaðýnda oksit tabakasý oluþumu, kaynak bölgesinde segregasyon meydana gelmesi ve seramik partiküllerin kaynak banyosu ile tepkimeye girmesi gibi nedenlerden dolayý sorunlar ortaya çýkmaktadýr. Bu sorunlar nedeniyle beklenen mekanik özellikler elde edilememektedir. Bu çalýþmada, SiC takviyeli alüminyum 2014 alaþýmýnýn kaynak edilebilirliði araþtýrýlmýþtýr. AlSi5 alaþýmý tel kullanýlarak, MIG yöntemiyle yapýlan kaynak iþlemlerinde farklý türde ve farklý deðerlerde kaynak akýmlarý kullanýlmýþtýr. Manuel kaynak akýmý ile elde edilen numuneler ile pulse kaynak akýmý ile elde edilen numuneler mikroyapý ve sertlik daðýlýmý açýsýndan karþýlaþtýrýlmýþtýr. Farklý kaynak akým türünün ve deðerlerinin kaynak mikroyapý ve sertlik daðýlýmý üzerindeki etkisi incelenmiþtir. Alüminyum 2014 matrisli ve SiC partikül takviyeli kompozitin kaynaðýnda pulse akým kullanýlmasý sonucunda, kaynak bölgesinde meydana gelebilecek segregasyon önlenmiþ, mikroyapý özelliklerinin iyileþtiði tespit edilmiþtir.